Materialning qattiqligi (issiqlik bilan ishlov berishdan oldin va keyin)

A. Materiallarning qattiqligining qiymatlari

qattiqligi
HRC qiymati		 qattiqligi
HRB qiymati
 qattiqligi
qiymati
Vickers
 qattiqligi
qiymati
Brinell
 N / mm2 DIN belgilar
-20 67 114 114 400 C15
-9 74 131 131 460 C10
1 83 154 156 560 C40 zanglamaydigan 303
10 90 183 182 635
15 93 199 200 680 C55 42CrMo4 32CrMo12
20 97 221 224 760 34CrNiMo6 14NiCr14
25 101 250 249 850 34CrNiMo6 oldindan davolangan
30 105 278 276 955
35 109 320 323 1110
40 112 385 370 1270
45 115 460 427 1453  C40
qotdi
50 118 535 497 1670 34CrNiMo6
qotdi		 32NiCrMo45
qotdi		 42CrMo4 qotdi
55 639 545 1870 C35 qotdi
57 694 576 1940
60 746 601 2110 14NiCr14
qotdi		 C10
qotdi
63 867 652 2220 32CrMo12
nitritlangan
65 940 682 2300
67 1060 725 2400
70 1170 760 2640

B. Materialning qattiqligi (issiqlik bilan ishlov berish)

Quyidagi jadvalda viteslarni termik ishlov berishda ishlatiladigan turli xil jarayonlar ko'rsatilgan
ashyo
Karburizatsiya
Qattiqlashuv
harorat
Söndürme
usul
qattiqligi
daraja
olingan
Tempering
Söndürüldü
C40 830/860 ° S
210 dan 230 ° C gacha ushlab turing
uchun yog'li hammomda
1 soat / 25 mm
40-45 soat
 650 ° C da ushlab turing
+ Bir soat sovutib oling
pechda yoki ochiq havoda
C55 810/840 ° S
210 dan 230 ° C gacha ushlab turing
uchun yog'li hammomda
1 soat / 25 mm
40-45 soat
 650 ° C da ushlab turing
+ bir soat davomida salqin
pechda yoki ochiq havoda
42CrMo4 860/890 ° S
210 dan 230 ° C gacha ushlab turing
uchun yog'li hammomda
1 soat / 25 mm
40-45 soat
 690 ° C da ushlab turing
+ bir soat davomida salqin
pechda yoki ochiq havoda
34CrNiMo6 820/850 ° S
180à200 ° C da ushlab turing
uchun yog'li hammomda
1 soat / 25 mm
40-45 soat
 650 ° C da ushlab turing
+ bir soat davomida salqin
pechda yoki ochiq havoda
Sementatsiya
C10 <Ø100
Ushlab turing
900 dan 930 ° Cgacha
1 soat davomida
tsementlash chuqurligi 0,2 mm
 770/790 ° S
Ushlab turing
150 dan 200 ° Cgacha
yog'li hammomda
1 soat / 25 mm
55-60 soat
 650 ° C da ushlab turing
+ bir soat davomida salqin
pechda yoki ochiq havoda
C10> Ø100
Ushlab turing
900-930 ° C
1 soat davomida
tsementlash chuqurligi 0,2 mm
 900/930 ° S
150 dan 200 ° C gacha ushlab turing
yog'li hammomda
1 soat / 25 mm
57-62 soat
 650 ° C da ushlab turing
+ bir soat davomida salqin
pechda yoki ochiq havoda
12NiCr14
900-930 ° S haroratda ushlab turing
1 soat davomida
tsementlash chuqurligi 0,2 mm
 820/840 ° S
150 dan 200 ° C gacha ushlab turing
yog'li hammomda
1 soat / 25 mm
57-62 soat
 650 ° C da ushlab turing
+ bir soat davomida salqin
pechda yoki ochiq havoda
* 250 dan 450 ° C gacha bo'lgan haroratda saqlamang yoki ishlatmang
Barcha qiymatlar taxminiy